RTV-2 Silicone Rubber, Silicone Rubber, Molding Silicone manufacturer / supplier in China, offering RTV-2 Tin Cured Silicone Rubber, Best Price Silicone for Mold Making Rubber, Liquid Silicon Rubber (HY630) and so on.

1
    YRS
General Supplier
Supplier Homepage Chemicals Rubber & Rubber Products Rubber Materials China Silicon Rubber Liquid Rubber Silicone Liquid Rubber Silicone for Fabric Coati

China Silicon Rubber Liquid Rubber Silicone Liquid Rubber Silicone for Fabric Coati

Get Latest Price
Min. Order / Reference FOB Price
200 kg US $12.80/ kg
Local Area: Shenzhen, Guangdong, China
R&D Capacity: OEM, ODM, Other
Payment Terms: LC, T/T, PayPal, WesternUnion
Material: Silicone Rubber
Appearance: Liquid
Place of Origin: Guangdong, China (Mainland)
Fabric Coating Liquid Rubber Silicone is a 2-part liquid silicone with high trFeeder ansparency, great tear-strength and strong bonding force.Fabric Coating Liquid Rubber Silicone Specification:
-Low shrinkage(<0.1%)
-Good skid-proof effect and high adhesive strength
-Wearproof, wash-rElectromagnetic Equipment esistant, high temperature resistant
-Non-toxic and odorless, foGas Generation Equipment & Parts od grade silicone
-High transparency and good tear-strength.Fabric Coating Liquid Rubber Silicone Application:
Fabric Coating Liquid Rubber Silicone is specially used for skid-proof purpose of frilalsAuto Repair Equipment & Tools , underclothes and widely applied for cotton fabric, polyester-mixed cotton cloth, nylon cloth, flax, woolen, insulating cloth, etc.Fabric Coating Liquid Rubber Silicone Datasheet:
ModelTB3140
AppearanceTransparent
Hardness(shore A)20± 2
Mix ratio(A: B)1: 1
Viscosity(mPa. S)60000~100000
Tensile strength(Mpa)4.6
Tear-strength(KN/m)19± 2
Elongation(%)360
Pot life/working time(25)12-24 hours
Curing time(100-120)10~20(mins)Fabric Coating Liquid Rubber Silicone Operation introduction:
1, Mix Part A and Part B as ratio 1: 1, you may add additive such as pigment as ratio 1~2% into part A.
2, It can be cured by heating with 100~150 degree, the curing time will be 5~10 minutes.Model
TB0330
Appearance
Transparent
Hardness(shore A)
30 ± 2
Mix ratio(A:B)
1:1
Viscosity(mPa.s)
60000~100000
Tensile strength(Mpa)
4.6
Tear-strength(KN/m)
19 &pluConnector & Terminals smn; 2
Elongation(%)
360
Pot life/working time(25C )
12-24 hours
curing time(100-120C )
10~20(mins)